Influence of Annealing Time Variation on Crystal Structure and Morphology of Oxide Material Nd1.2FeO3 by Solid-State Reaction Method

Sujiono, Eko Hadi and Said, A.C.M and Dahlan, M.Y. and Imran, R.A and Samnur, Samnur (2018) Influence of Annealing Time Variation on Crystal Structure and Morphology of Oxide Material Nd1.2FeO3 by Solid-State Reaction Method. In: IOP Conference Series: Materials Science and Engineering.

	Text (Artikel) 29_Prosiding Internasional-Influence of Annealing Time Variation on Crystal Structure and Morphology of Oxide Material NdFeO3.pdf Download (995kB)
	Text (Peer Review) 29_Peer Review Prosiding Internasional-Influence of Annealing Time Variation on Cystal Structure and Morphology.pdf Download (935kB)
	Text (Turnitin) 29_Turnitin Prosiding Internaional-Influence of Annealing Time Variation on Crystal Structure and Morphology of Oxide Material NdFeO3.pdf Download (548kB)
	Text (Korespondensi) 29_Korespondensi prosiding internasional-Influence of Annealling Time Variation of Crystal Structure And Morphology From Oxide Material.pdf Download (594kB)

Abstract

NdFeO3 is one of the oxide material can be detected various gases, like S/O2, CO, H2S, etc. In this research, Nd1.2FeO3 as oxide material have been synthesized by solid-state reaction with a variation of annealing time. Characterized by XRD shows that the samples have form crystal perovskite structure with dominant phase and peak intensity correspond to hkl (121). FWHM value for the dominant peak was 0.22°. The crystallite of the samples was determined using Debye Scherer formula were 393.08, 393.10, and 393.10 nm, respectively. While the SEM characterized showed the morphology of the samples was homogenous with grain size estimates of 0.2μm. These results indicate the variation of annealing time 1, 2, and 3 hours did not significantly affect the crystallinity and morphology of Nd1.2FeO3 oxide material.

Item Type:	Conference or Workshop Item (Paper)
Subjects:	FAKULTAS TEKNIK FAKULTAS TEKNIK > Pendidikan Teknik Mesin KARYA ILMIAH DOSEN Universitas Negeri Makassar > KARYA ILMIAH DOSEN
Divisions:	FAKULTAS TEKNIK
Depositing User:	Mardiana Mardiana
Date Deposited:	24 Apr 2023 11:54
Last Modified:	24 Apr 2023 11:54
URI:	http://eprints.unm.ac.id/id/eprint/27973

Actions (login required)

View Item